Description:
PM® 206 is a room temperature self-crosslinking waterborne emulsion for decorative wood coating, providing excellent adhesion on various substrates including PU, NC, alkyd, Al, Fe, and cement etc., and providing excellent water resistance and chemical resistance including alcohol, tea, alkali, vinegar, and ink. And this product is zero VOC, and very suitable for family, hotel decoration and renovation.
Product specifications:
|
Appearance
|
White milky emulsion
|
|
N.V.M
|
42±0.5 %
|
|
Particle Size
|
75±5 nm
|
|
pH
|
8.0-9.0
|
Application:
Family, hotel decoration and renovation.
Package and Storage:
18KG or other scale; the shelf time is no less than 6 months at the normal conditions.
Description:
PM® 207 is a latex with core-shell structure and the room temperature self-crosslinking ability, providing equivalent hardness as DOW 3311. Under the same conditions the drying speed of this product is very fast, providing better chemical resistance with good adhesion, is very suitable for wood furniture and decoration.
Product specifications:
|
Appearance
|
White milky emulsion
|
|
N.V.M
|
42±0.5 %
|
|
Particle Size
|
85±5 nm
|
|
pH
|
8.0-9.0
|
Application:
PM® 207 can be used as topcoat of wood coatings.
Package and Storage:
18KG or other scale; the shelf time is no less than 6 months at the normal conditions.
Description:
PM® 210 is a universal emulsifier-free hydroxyl acrylic copolymer emulsion for used in 2K PU systems that develops very good film with the addition of a certain amount of water-dispersible isocyanate crosslinkers at room temperature or under mild curing conditions. This product has some special properties, such as good flow and wetting properties on wood or other substrates with low foaming tendency. The formed film after curing has features of good transparence, excellent hardness, and outstanding water, household chemicals resistance.
Product specifications:
|
Appearance
|
Semi-transparent liquid
|
|
N.V.M
|
40±2 %
|
|
Viscosity (Brookfield, 25 oC)
|
< 1500 mPa?s
|
|
Free monomers
|
< 1000 ppm
|
|
pH
|
7.5-9.0
|
Application:
PM® 210 can be used as topcoat of wood coatings, PU floor coatings, auto refinish coatings, adhesion and texture in 2K PU systems.
Formulating guidelines:The hydroxyl group of DISPER 210 is about 2% by weight. The recommended weight ratio of DISPER 210 to water-dispersible isocyanate crosslinkers (such as DISPER 504 with about 22% –NCO group by weight) is (8-10) : 1.
Package and Storage:
18KG or other scale; the shelf time is no less than 6 months at the normal conditions.
Description:
PM® 212 is a self crosslinking, modified acrylic copolymer emulsion for used in industrial wood finishes that develops very good film without additional crosslinkers at room temperature or under mild curing conditions. The formed film has features of good transparence, high gloss, excellent block resistance, excellent water, household chemicals and wet heat resistance, as well as good weatherability, scratch resistance, and sanding performance, etc.
Product specifications:
|
Appearance
|
White milky emulsion
|
|
N.V.M
|
45±2 %
|
|
Viscosity (Brookfield, 25 oC)
|
< 500 mPa?s
|
|
Free monomers
|
< 1000 ppm
|
|
pH
|
7.5-8.5
|
Application:
PM® 212 is compatible with other types of acrylic copolymer emulsion and urethane dispersions. DISPER 212 can be used as topcoat of wood coatings.
Formulating guidelines:
The MFFT of DISPER 212 is about 30 oC. It’s better to be used with a certain amount of coalescents (e.g. butylglycol or butyldiglycol) for good film formation.
Package and Storage:
18KG or other scale; the shelf time is no less than 6 months at the normal conditions.
Description:
PM® 214 is a self crosslinking, emulsifier-free acrylic copolymer emulsion for used in industrial wood finishes that develops very good film without additional crosslinkers at room temperature or under mild curing conditions. This product has some special properties, such as good flow and wetting properties on wood, with low foaming tendency. The formed film has features of good transparence, high gloss, excellent block resistance, excellent water, household chemicals resistance.
Product specifications:
|
Appearance
|
White milky emulsion
|
|
N.V.M
|
40±2 %
|
|
Viscosity (Brookfield, 25 oC)
|
< 500 mPa?s
|
|
Free monomers
|
< 1000 ppm
|
|
pH
|
8.0-9.0
|
Application:
PM® 214 can be used as topcoat of wood coatings. It also can be used in plastic coating.
Formulating guidelines:
The MFFT of DISPER 214 is about 33 oC. It’s better to be used with a certain amount of coalescents (e.g. butylglycol or butyldiglycol) for good film formation.
Package and Storage:
18KG or other scale; the shelf time is no less than 6 months at the normal conditions.
Description:
PM® 504 is a universal solvent-free water-dispersible isocyanate crosslinker based on HDI that develops very good film with the combination of a certain amount of polymeric compounds containing hydroxyl group, such as hydroxyl acrylic emulsion, hydroxyl polyurethane dispersion, WB polyester or WB alkyd resins in 2K PU systems. The formed film after curing has features of excellent balance of hardness and flexibility, good transparency, and outstanding water and household chemicals resistance.
Product specifications:
|
Appearance
|
Slightly yellow clear liquid
|
|
Viscosity (Brookfield, 25 oC)
|
2000-4500 mPa?s
|
|
-NCO content (wt%)
|
21%-23%
|
|
Colour (Gardner, Fe-Co)
|
≤1
|
Application:
PM® 504 can be used as isocyanate hardener in WB 2K PU systems.
Formulating guidelines:
The recommended mole ratio of –NCO group of DISPER 504 to hydroxyl group is (1.1-1.3):1.
Package and Storage:
18KG or other scale; the shelf time is no less than 6 months at the normal conditions.