Description:
PM® 301 is non-silicone leveling agent with 70% active fluorin-containing polyacrylate which have good wetting, flow and leveling properties. Improves hand feel and effectively prevents defects such as crater, pin hole, and fish eye and have no adverse effect on inter-layer adhesion or recoatability.
Chemistry: fluoro-modified acrylate copolymer
Product specifications:
|
Appearance
|
Transparent pale yellow liquid
|
|
N.V.M
|
70¡À2 %
|
|
Solvent
|
Xylene
|
|
Specific gravity
|
0.94g/cm3(25¡æ)
|
Application:
Polyester, PU, Epoxy and acrylic solvent-based coating
Dosage: 0.2-1% of total weight
Method of addition: Post-addition
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 302 is non-silicone leveling agent with 70% active polyacrylate which have good flow and leveling property. Effectively prevents defects such as crater, pin hole, and fish eye and have no adverse effect on inter-layer adhesion or recoatability.
Chemistry: Acrylic copolymer
Product specifications:
|
Appearance
|
Transparent pale yellow liquid
|
|
N.V.M
|
70¡À2 %
|
|
Solvent
|
Xylene
|
|
Specific gravity
|
0.91g/cm3(25¡æ)
|
Application:
Solvent-based coating
Dosage: 0.2-1% of total weight
Method of addition: Post-addition
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 303 is 1% active solution of silicone defoamer for non-solvent and solvent-borne coatings, printing inks. Standard silicone defoamer for all solvent-borne systems. Good balance between effectiveness and compatibility.
Chemistry: Flouro-modified silicone
Product specifications:
|
Appearance
|
Transparent pale liquid
|
|
N.V.M
|
1¡À0.2 %
|
|
Solvent
|
Acetone
|
|
Specific gravity
|
0.79g/cm3(25¡æ)
|
Application:
Non-solvent and solvent-based coatings and inks
Dosage: 0.1-1% of total weight
Method of addition: Post-addition
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 304 is 100% active defoamer with silicone fluid and powdered silica. Suitable for solvent base and non-solvent system, exhibiting excellent defoaming property with low dosage. Especially for high viscosity and color coatings and inks.
Chemistry: Silica-containing silicone fluid
Product specifications:
|
Appearance
|
Opaque pale white liquid
|
|
N.V.M
|
>99 %
|
|
Viscosity(cps)
|
1000-1250
|
|
Specific gravity
|
0.93g/cm3(25¡æ)
|
Application:
Non-solvent and solvent-based coatings and inks
Dosage: 0.1-1% of total weight
Method of addition: Post-addition
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 305 is 80% active polyester designed for improving adhesion of paint film especially on non-ferrous substrates and mainly used in stoving coatings.
Chemistry: Branched Polyester
Product specifications:
|
Appearance
|
Transparent pale yellow liquid
|
|
N.V.M
|
80¡À2 %
|
|
Solvent
|
IPA
|
|
Acid value(mg KOH/g)
|
60-80
|
|
Specific gravity
|
0.81g/cm3(25¡æ)
|
Application:
Alkyd/melamine, Acylate/melamine, Solvent-based coating
Dosage: 0.5-2% of total weight
Method of addition: Post-addition
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Descripti, on:
PM® 306 is 50% active phosphoric polyester dispersant designed for inorganic pigments such as TiO2 in solvent-based coatings and printing inks. It allows for higher pigment loading while keeping the coatings at a good flow and storage stability.Strong reduction of millbase viscosity.
Chemistry: Phosphoric polyester
Product specifications:
|
Appearance
|
Transparent pale liquid
|
|
N.V.M
|
50¡À2 %
|
|
Solvent
|
PMA
|
|
Acid value(mg KOH/g)
|
130-150
|
|
Specific gravity
|
0.86g/cm3(25¡æ)
|
Application:
1. Solvent borne TiO2 concentrate£»
2. Solvent based automotive, wood, coil, and industrial coatings
2. Method of addition and Dosage:
1£© PM® 306 should be added before the loading of pigments during the milling procedure£»
2£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
TiO2
|
2-4%
|
|
Inorganic pigments
|
5-10%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 307 50% active polymeric dispersant for solvent-based coatings and pigment concentrates. Stabilizes pigments of all types. Broad compatibility for all-purpose solvent-borne pigment concentrates on the basis of aldehyde and acrylate grinding resins.
Chemistry: Pu based polyester
Product specifications:
|
Appearance
|
Transparent pale liquid
|
|
N.V.M
|
50¡À2 %
|
|
Solvent
|
BAC
|
|
Specific gravity
|
0.99g/cm3(25¡æ)
|
Application:Solvent-based coatings and inks£»
2.Automotive, wood and industrial paints
Method of addition and Dosage:
3£© PM® 307 should be added before the loading of pigments during the milling procedure£»
4£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨Dispersant/Pigments£©
|
|
Organic pigments
|
8-12%
|
|
Carbon black
|
10-40%
|
|
High BET carbon black
|
40-100%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 308 is 100% active polymeric dispersant designed for inorganic pigments such as TiO2 and iron oxide in solvent-based ink. It allows for higher pigment loading while keeping the ink at a good flow and storage stability.
Chemistry: Polyester
Product specifications:
|
Appearance
|
Wax paste/viscous liquid
|
|
N.V.M
|
>99 %
|
|
Gardner color
|
14 max
|
|
Flash point
|
230¡æ
|
|
Specific gravity
|
0.91g/cm3(25¡æ)
|
Application:
1) For grinding inorganic pigment.
2) PVC paste for plastics and solvent based ink.
Method of addition and Dosage:
5£© PM® 308 should be added before the loading of pigments during the milling procedure£»
6£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
TiO2
|
2-4%
|
|
Inorganic pigments
|
5-10%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 309 is 100% active polymeric dispersant for organic and inorganic pigment dispersion in solvent-based system, with low product dosage, efficient dispersion of the organoclay powder, low foaming properties, and excellent stability performance when used in a pre-gel
Chemistry: Polyamine polyester
Product specifications:
|
Appearance
|
Brown viscous liquid
|
|
N.V.M
|
>99%
|
|
Gardner color
|
14 max
|
|
Flash point
|
260¡æ
|
|
Specific gravity
|
0.94g/cm3(25¡æ)
|
Application:
1) Organic red and yellow pigments and medium-low surface area carbon black.
2) Industrial coating3) Solvent-based printing ink
Method of addition and Dosage:
7£© PM® 309 should be added before the loading of pigments during the milling procedure£»
8£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
Organic pigments
|
8-12%
|
|
Carbon black
|
10-40%
|
|
High BET carbon black
|
40-100%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 310 is 100% active polymeric dispersant which will improve pigment dispersion stability in liquid organic media.
Chemistry: Polyamine polyester
Product specifications:
|
Appearance
|
Wax paste/viscous liquid
|
|
N.V.M
|
>99 %
|
|
Gardner color
|
14 max
|
|
Flash point
|
188¡æ
|
|
Specific gravity
|
0.93g/cm3(25¡æ)
|
Application:
1) Offset inks
2) Publication gravure inks
Method of addition and Dosage:
9£© PM® 310 should be added before the loading of pigments during the milling procedure£»
10£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
TiO2
|
2-4%
|
|
Inorganic pigments
|
5-10%
|
|
Organic pigments
|
20-40%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 311 is 100% active polymeric dispersant designed to achieve a blue tone ultra high black for carbon black.It also shows very good result dispersing other organic pigments for superior tinting strength,gloss,and rheological property.
Chemistry: Polyamine polyester
Product specifications:
|
Appearance
|
Amber waxy granules
|
|
N.V.M
|
>99%
|
|
Gardner color
|
9 max
|
|
Melting point
|
45¡æ
|
|
Specific gravity
|
0.94g/cm3(25¡æ)
|
Application:
1) Automotive and Industrial paints (Solvent based)
2) Packaging gravure inks
Method of addition and Dosage:
11£© PM® 311 should be added before the loading of pigments during the milling procedure£»
12£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
Organic pigments
|
8-12%
|
|
Carbon black
|
10-40%
|
|
High BET carbon black
|
40-100%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 312 is 100% active polymeric dispersant which will improve pigment dispersion and stability in liquid organic media, and is recommended for use in solvent-based pigment concentrates for general industrial paints.
Chemistry: Polyamine polyester
Product specifications:
|
Appearance
|
Amber-brown viscous liquid
|
|
N.V.M
|
>99%
|
|
Gardner color
|
14 max
|
|
Flash point
|
236¡æ
|
|
Specific gravity
|
0.94g/cm3(25¡æ)
|
Application:
1) Automotive and Industrial paints (Solvent based)
2) Packaging gravure inks
Method of addition and Dosage:
13£© PM® 312 should be added before the loading of pigments during the milling procedure£»
14£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
Organic pigments
|
8-12%
|
|
Carbon black
|
10-40%
|
|
High BET carbon black
|
40-100%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.
Description:
PM® 313 is 40% active polymeric dispersant designed to have a broadbased resin compatibility. It shows outstanding performance in grinding carbon black as well as organic pigments in solvent paint for superior tinting strength,gloss,and rheological property.
Chemistry: Polyamine polyester
Product specifications:
|
Appearance
|
Brown liquid
|
|
N.V.M
|
40%
|
|
Gardner color
|
11 max
|
|
Solvent
|
BAC
|
|
Specific gravity
|
0.98g/cm3(25¡æ)
|
Application:
1)For solvent paint to grind high surface carbon black and organic pigments.
2)Automtive paint,plastic
Method of addition and Dosage:
15£© PM® 313 should be added before the loading of pigments during the milling procedure£»
16£© Dosage£¨The optimal dosage should be based on the experiments£¡£©
|
Pigments
|
%£¨dispersant/pigments£©
|
|
Organic pigments
|
8-12%
|
|
Carbon black
|
10-40%
|
|
High BET carbon black
|
40-100%
|
Package and Storage:
25KG or other scale; the shelf time is no less than 2 months at the normal conditions.